倒角:

Protective as needed

有效孔徑 (%):

85

鍍膜:

S1: DLC Coating

S2: BBAR (3000-5000nm)

邊緣:

Fine Ground

鍍膜規(guī)格:

AR: Ravg ≤0.5% @ 3000 - 5000nm

努氏硬度 (kg/mm2) :

1150

基材:

Silicon (Si)

平行度（弧分）:

<3

表面平整度:

λ/10 @ 10.6μm

波長范圍 (nm):

3000 - 5000

表面質量:

40-20

Coating Adhesion:

AR: per MIL-C-48497C

DLC: per MIL-C-48497C

Coating Salt Spray:

AR: N/A

≥72 Hours per MIL-C-675

Coating Solubility and Cleaning:

AR: per MIL-C-48497

DLC: per MIL-C-48497

Coating Abrasion:

AR: Moderate, per MIL-C-48497C

DLC: Severe, per MIL-C-48497C

Coating Salt Solubility:

AR: N/A

DLC: ≥24 Hours Immersion per MIL-C-675C

Coating Humidity:

AR: 24 Hours per MIL-C-48497C

DLC: 24 Hours per MIL-C-48497C

Coating Wiper Durability:

AR: N/A

DLC: ≥1,000 Wipes of Sand/Slurry per TS-1888

Coating Temperature (°F):

AR: -80 to +160 per MIL-C-48497C

DLC: -80 to +160 per MIL-C-48497C

注意
:

Arrow on substrate edge points towards DLC coated surface

Dia. (mm)

厚度 (mm)

鍍膜

產品編碼

25.40

2.00

S1: DLC Coating

S2: BBAR (3000-5000nm)

#16-816

50.80

3.00

S1: DLC Coating

S2: BBAR (3000-5000nm)

#16-817

76.20

3.00

S1: DLC Coating

S2: BBAR (3000-5000nm)

#16-818

Coating Specifications

Specification

AR Coating

DLC Coating

Adhesion

per MIL-C-48497C

per MIL-C-48497C

Abrasion

Moderate, per MIL-C-48497C

Severe, per MIL-C-48497C

Humidity

24 Hours per MIL-C-48497C

24 Hours per MIL-C-48497C

Salt Solubility

-

≥24 Hours Immersion per MIL-C-675C

Salt Spray

-

≥72 Hours per MIL-C-675

Temperature (°F)

-80 to +160 per MIL-C-48497C

-80 to +160 per MIL-C-48497C

Solubility and Cleaning

per MIL-C-48497

per MIL-C-48497

Wiper

-

≥1,000 Wipes of Sand/Slurry per TS-1888

Coating Temperature (°F)

-80 to +160 per MIL-C-48497C

-80 to +160 per MIL-C-48497C